PLEXIGLAS® Sheet Soundstop GS CC
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | PLEXIGLAS® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7TLdMl_PLEXIGLAS-Sheet-Soundstop-GS-CC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PLEXIGLAS® Soundstop GS CC is a highly transparent grade of cast acrylic with embedded polyamide threads. In the event of breakage due to an accident, these threads retain any sheet fragments and prevent them from falling down. Applications: These properties make PLEXIGLAS® Soundstop GS CC especially suitable for :
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1B/5 |
| Tensile Stress 1 | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/1B/5 |
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.37 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ISO 306/B |
| CLTE - Flow (0 to 50°C) | 7.0E-5 | cm/cm/°C | DIN 53752-A |
| Maximum Service Temperature | 70 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Light Transmission - of clear- transparent elements | > 92 | % | DIN 5036 |
| Weight per Unit Area (1.50 cm) | 17.8 | kg/m² | |
| Weighted Sound Reduction Index | 32 dB at 20 mm 30 dB at 15 mm 33 dB at 25 mm | EN 1793-2 | |
| Silver Retention: By means of embedded polyamide threads (EN 1794-2, Annex B) |
| Note Message | |
|---|---|
| 1 . | Type 1B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® EXT | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| FHR Polypropylene P5M6N-058A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Karina CLEAR PVC COMPOUND -E 80/314-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OnFlex™ BIO 5380A-E0006 | PolyOne Corporation | TPE | OnFlex™ BIO |
| 3M™ Dyneon™ PTFE Compound TF 6712 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |