LG ABS HI153
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BpGg87_LG-ABS-HI153.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS HI153 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of LG ABS HI153 are:
The typical application areas of LG ABS HI153 are: electrical/electronic applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 48 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2430 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 69 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 69 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 200 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 6 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2022TN00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TECHNYL® 2710IR BRIGHT | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Wellamid® GF33-66/6 XE-NBK1 | Wellman Engineering Resins | Nylon 66/6 | Wellamid® |
| ULTEM™ STM1700 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Colorite 12 Series 8012 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |