Clariant Nylon 6/6 PA-111N40

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Clariant Corporation
Trademark:	Clariant Nylon 6/6
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BocUmr_Clariant-Nylon-6-6-PA-111N40.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Clariant Nylon 6/6 PA-111N40 is a polyamide 66 (nylon 66) material, which contains 15% glass fiber reinforced materials and 25% mineral fillers. This product is available in North America and is processed by injection molding.

The main features of Clariant Nylon 6/6 PA-111N40 are:

flame retardant/rated flame

Flame Retardant

Low shrinkage

high strength

Good processability

Typical application areas include:

Wire and cable

marine applications

building applications

military applications

Automotive Industry

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight Mineral filler, 25% filler by weight
Features	Good dimensional stability Low warpage Rigidity, high High strength Antistatic property Workability, good Good corrosion resistance Good coloring Good chemical resistance Good toughness Low shrinkage Low or no water absorption Flame retardancy
Uses	Ship application Architectural application field Metal substitution Military application Application in Automobile Field Sporting goods Medical/nursing supplies
Agency Ratings	UL 94
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.49	g/cm³	ASTM D792
Molding Shrinkage - Flow (3.18 mm)	0.35	%	ASTM D955
Water Absorption (24 hr)	0.70	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ASTM D785
Class m	98		ASTM D785
Class r	120		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	145	MPa	ASTM D638
Tensile Elongation (Break)	4.0	%	ASTM D638
Flexural Modulus	9650	MPa	ASTM D790
Flexural Strength	214	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	48	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	254	°C	ASTM D648
1.8 MPa, not annealed	239	°C	ASTM D648
CLTE - Flow	3.8E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+14	ohms·cm	ASTM D257
Dielectric Strength	19	kV/mm	ASTM D149

Flammability	Nominal Value	Unit	Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	79.4	°C
Drying Time	2.0 - 4.0	hr
Suggested Max Moisture	0.20	%
Rear Temperature	266 - 293	°C
Middle Temperature	266 - 293	°C
Front Temperature	266 - 293	°C
Processing (Melt) Temp	266 - 288	°C
Melt Temperature (Aim)	274	°C
Mold Temperature	65.6 - 93.3	°C
Injection Rate	Fast
Back Pressure	0.345 - 0.689	MPa
Screw Speed	20 - 100	rpm
Cushion	3.18 - 6.35	mm

Injection instructions
Injection Pressure: Use minimum pressure to achieve 95% fill during the boost inj. pressure phase.Hold Pressure: 30% to 75% of injection pressure.Mold Temp. Target: 180°FScrew Speed Target: 75 RPM

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3570	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
TEREZ PA 6.6 7510 GF30	TER HELL PLASTIC GMBH	Nylon 66	TEREZ PA 6.6
Cosmic DAP K61/6230	Cosmic Plastics, Inc.	DAP	Cosmic DAP
Duratuf™ 909	Technical Polymers, LLC	Acetal (POM) Homopolymer	Duratuf™
Sylvin 9655-60 Clear 876	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin