TAIRIPRO F4008
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRIPRO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BmA1f6_TAIRIPRO-F4008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC PP resin F4008 meets the requirements of FDA, RoHS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 200 | % | ASTM D638 |
| Flexural Modulus (23°C) | 834 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.35 mm) | 85.0 | °C | ASTM D648 |
| Extrusion instructions |
|---|
| Screw Temp: 190 - 220° CCasting Roll: 30°CCooling Water Temperature: 30°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SolVin 178GI | INOVYN | PVC, Unspecified | SolVin |
| SUSTAMID 6G PLUS | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Geon™ HTX M6220 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| EMOPLEN® HP MTF 30 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |
| Karina E 1000/ HMB 21586 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |