Hanwha Total PE 6200F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BlG4bx_Hanwha-Total-PE-6200F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6200F is a linear low-density polyethylene resin for heavy duty films for packaging. This grade is designed to be processed in conventional blown film equpment. 6200F is a hexene comonomer grade. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.8 | MPa | ASTM D882 |
| TD : Yield | 10.8 | MPa | ASTM D882 |
| MD : Fracture | 42.2 | MPa | ASTM D882 |
| TD : Fracture | 34.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 580 | % | ASTM D882 |
| TD : Fracture | 760 | % | ASTM D882 |
| Dart Drop Impact | 240 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 270 | g | ASTM D1922 |
| TD : 25 µm | 520 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 55 | ASTM D2457 | |
| Haze | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 190 | °C | |
| Cylinder Zone 2 Temp. | 170 - 190 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Cylinder Zone 4 Temp. | 170 - 190 | °C | |
| Cylinder Zone 5 Temp. | 170 - 190 | °C | |
| Die Temperature | 190 - 200 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1 to 2 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0335T40V | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Filter-bond™ E-3505 | Hapco Inc. | TS, Unspecified | Filter-bond™ |
| Laprene® 830000913 | SO.F.TER. SPA | SEBS | Laprene® |
| LNP™ THERMOCOMP™ WF0039U compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| Formolon® AWS | Formosa Plastics Corporation, U.S.A. | PVC, Unspecified | Formolon® |