Shell Shock® Slow
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Shell Shock® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BkYO8B_Shell-Shock-Slow.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shell Shock® FAST and Shell Shock® SLOW are thixotropic plastics that self thicken when mixed and can be brushed onto a variety of surfaces or into rubber molds. When Parts A and B are mixed in proper proportion (1A:4B by volume or 1A:5B by weight), material cures at room temperature with virtually no shrinkage to a hard, durable plastic that exhibits good compressive and flexural strength. Fully cured castings are rigid and can be sanded, primed and painted. Color effects are possible by adding SO-Strong Color Tints. Shell Shock® plastics are ideal for making fast, lightweight rigid molds for creating silicone appliances and effects (use as a replacement for ‘stone molds'). You can also brush a "gel coat" into a rubber mold and back it up with rigid foam, creating a highly detailed lightweight casting. These products can also be brushed onto styrofoam (polystyrol) as an impact resistant coating that can be sanded, primed and painted (minimum 3 coats recommended). Shell Shock® plastics can also be used to make rigid support shells for brush on rubber molds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.625 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 1A:5B by weight 1A:4B by volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.060 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ASTM D638 |
| Tensile Strength | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.40 | % | ASTM D638 |
| Flexural Modulus | 6760 | MPa | ASTM D790 |
| Flexural Strength | 49.3 | MPa | ASTM D790 |
| Compressive Modulus | 3450 | MPa | ASTM D695 |
| Compressive Strength | 62.1 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 57.2 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 8.0 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 3000 | cP | ASTM D2393 |
| Demold Time (23°C) | 300 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 153 SP20 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| Unipren® Elastomers B3 NTLA010 55A UP310 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Nylene® 5213-02 | Custom Resins Group | Nylon 6 | Nylene® |
| Badamid® T70 GF30 FR HF | Bada AG | Nylon 6/6T | Badamid® |
| APEX® 3800-80NT1 | Teknor Apex Company | PVC, Flexible | APEX® |