ISPLEN® PC 474 AV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pfHmXP_ISPLEN-PC-474-AV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ISPLEN® PC474 AV is a polypropylene copolymer compound, charged with 40% calcium carbonate and high melt flow rate. ISPLEN® PC474 AV shows good impact strength an a medium rigidity. It gives high stiffness, and a low warpage and shrinkage behaviour. This product is UV stabilised an antistatic formulated. APPLICATIONS Aesthetic applications which require good gloss surface.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 1.1 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 2.60 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 19 | % | ISO 527-2 |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 1.0 | kJ/m² | |
| -20°C | 1.4 | kJ/m² | |
| 0°C | 1.5 | kJ/m² | |
| 23°C | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 12 | kJ/m² | |
| -20°C | 15 | kJ/m² | |
| 0°C | 41 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| 0°C | 2.5 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| 0°C | 15 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A120 |
| -- | 93.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| KYOCERA KE-1100A-S3 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| Hybrid S464 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| Latimass 62-01 D025 | LATI S.p.A. | Nylon 6 | Latimass |
| Karina BLUE PVC COMPOUND 810-06/115-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| 3M™ Dyneon™ PTFE Compound TF 8637 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |