InnoTuf® HP-1085A
| Category: | TSU-Ester , Polyurethane Thermoset Elastomer, Polyester Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BTiCGs_InnoTuf-HP-1085A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-1085A is a high performance 85 shore A polyester based polyurethane elastomer formulated for hand-batch or meter mix processing methods. Excellent physical properties can be obtained with a post cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.13 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 1.0 to 1.5 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 8.00 | mg | ASTM D4060 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (Split) | 18 | kN/m | ASTM D470 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 72 Mix Ratio by Volume: 68 | ||
| Demold Time | 60 to 180 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 60°C 1 | 0.60 | Pa·s | |
| 38°C 2 | 0.70 | Pa·s | |
| 60°C 3 | 0.73 | Pa·s | |
| Curing Time 4 | 1.8E+2 | hr | |
| Gel Time | 10 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 80 to 90 | ASTM D2240 | |
| Tensile Strength | 31.0 | MPa | ASTM D638 |
| Tensile Elongation at Break | 800 | % | ASTM D638 |
| Tear Strength | 66.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Resin |
| 3 . | Hardener |
| 4 . | 16 hours at 150°F + 7 days at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3457 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Algoflon® L105 | Solvay Specialty Polymers | PTFE | Algoflon® |
| Karina BLACK PVC COMPOUND -E 880-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® NA214000 | LyondellBasell Industries | LDPE | Petrothene® |
| Elastocon® CLR15 | Elastocon TPE Technologies | TPE | Elastocon® |