Shuang-Bang CD-1202
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Shuang-Bang Industrial Corp. |
| Trademark: | Shuang-Bang |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAbTLd_Shuang-Bang-CD-1202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
One component PU Resins PU membrane is produced by coating the resin on substrate and drying it to vaporize the solvent adequately. The membrane gives soft hand-feel and dry surface, and offers waterproof and windproof properties. Using one component type PU resin alone with adequate crosslinker for yarn fixation, following by drying process to vaporize solvent adequately, could form high yarn-bonding membrane. Shoes, leather bag, ready-make clothes Blocking resistance, high water resistance, good hand-feel High hardness resin. High brightness and hard hand-feel. Good abrasion resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Solvents | DMF/MEK |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Clear/Transparent | ||
| Solids Content | 29 to 31 | % | |
| Viscosity (25°C) | 70 to 100 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Modulus (100% Secant) | 17.2 to 22.1 | MPa | |
| Tensile Strength | > 44.1 | MPa | |
| Tensile Elongation at Break | > 200 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3880H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| NEOPLAST 240 FT EB | Zylog Plastalloys | TPV | NEOPLAST |
| Clariant PBT PBT-1100G20 | Clariant Corporation | PBT | Clariant PBT |
| Hyundai EP PA6 LS610 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| LNP™ THERMOCOMP™ DX07408 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |