Polidan® TUX 100
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Polidan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BFfYDb_Polidan-TUX-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLIDAN®TUX 100 is a kind of "SIOPLAS"®"High-density crosslinkable polyethylene produced by the process. It is dedicated to the production of cross-connected pipes of various diameters and wall thicknesses. POLIDAN®The cross-linked polyethylene pipe produced by TUX 100 has the following excellent properties:-Excellent high temperature resistance
-Excellent long-term load strength POLIDAN calculated by EXOVA polymer according to ISO 9080®MRS grade of TUX 100. The results significantly exceeded the requirements of MRS level 10. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.953 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 2(190°C/5.0 kg) | 1.3 | g/10 min | ISO 1133 |
| Gel Content 3 | > 65 | % | EN 579 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1B/1 | ||
| -40°C | 3300 | MPa | ISO 527-2/1B/1 |
| 23°C | 1250 | MPa | ISO 527-2/1B/1 |
| 100°C | 130 | MPa | ISO 527-2/1B/1 |
| Tensile Stress | ISO 527-2/1B/50 | ||
| Yield, -40°C | 47.0 | MPa | ISO 527-2/1B/50 |
| Yield, 23°C | 26.0 | MPa | ISO 527-2/1B/50 |
| Yield, 100°C | 6.00 | MPa | ISO 527-2/1B/50 |
| Tensile Strain | |||
| Yield, -40°C | 7.0 | % | ISO 527-2/1B/50 |
| Yield, 23°C | 8.0 | % | ISO 527-2/1B/50 |
| Yield, 100°C | 16 | % | ISO 527-2/1B/50 |
| Fracture, -40°C | 110 | % | ISO 527-2/1B/25 |
| Fracture, 23°C | 390 | % | ISO 527-2/1B/25 |
| Fracture, 100°C | 170 | % | ISO 527-2/1B/25 |
| Flexural Modulus | ISO 178 | ||
| -40°C | 2600 | MPa | ISO 178 |
| 23°C | 1200 | MPa | ISO 178 |
| 100°C | 167 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 15 | kJ/m² | ISO 179/1A |
| -25°C | Partial fracture | ISO 179/1A | |
| 23°C | Partial fracture | ISO 179/1A | |
| 100°C | No Break | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.0 | °C | ISO 306/B50 |
| CLTE - Flow | |||
| -90 to-30°C 4 | 1.0E-4 | cm/cm/°C | |
| -100 to 100°C 5 | 1.4E-4 | cm/cm/°C | |
| -30 to 90°C 6 | 1.9E-4 | cm/cm/°C |
| Additional Information |
|---|
| 加工：POLIDAN® TUX 100与催化剂母粒 CATALYST CAT 10 按照95%：5%的比例一起使用。 POLIDAN® TUX 100化合物及其 Catalyst CAT 10 可以与高品质PE基色母粒一起使用。苏威特种聚合物建议在使用前与烘干所有色母粒。性能-用热水或蒸气对最终产品进行后处理，形成交联。存储和操作-为了防止过早交联，POLIDAN® TUX 100化合物及Catalyst CAT 10应分开存放，使用时混合。可教练化合物必须在开袋后6-8小时内使用。 产品应按照如下要求存放：-密封，包装袋完好 环境温度不超过40°C -室内放置，避免在阳光下曝晒 -存放时间过长会造成产品性状改变。苏威特种聚合物建议按照包装印制生产日期，在12个月内使用完毕。如果没有满足上述条件，苏威特种聚合物不承担任何责任。包装-POLIDAN® TUX 100以500kg/箱，内含一只防潮袋的方式供应。或用防潮袋包装，25kg/袋，1375kg/货板的形式供应。技术服务-POLIDAN® TUX 100属于苏威特种聚合物 POLIDAN®产品系列。苏威特种聚合物技术服务部门为客户提供包括投产和产品使用过程中任何必要的进一步信息和建议。 POLIDAN® TUX 100 和 CATALYST CAT 10 是苏威特种聚合物的商标，由Ineos Polyolefins许可生产、经销。 |
| Note Message | |
|---|---|
| 1 . | Use 95%Polidan®The mixture of TUX 100 and 5% CAT 10 catalyst is extruded into 18 × 2mm plastic tubes, cured in warm water at 95 °c for 12 hours, and the average value of all these plastic tube samples is taken. |
| 2 . | Use 95%Polidan®The mixture of TUX 100 and 5% CAT 10 catalyst is extruded into 18 × 2mm plastic tubes, cured in warm water at 95 °c for 12 hours, and the average value of all these plastic tube samples is taken. |
| 3 . | Use 95%Polidan®The mixture of TUX 100 and 5% CAT 10 catalyst is extruded into 18 × 2mm plastic tubes, cured in warm water at 95 °c for 12 hours, and the average value of all these plastic tube samples is taken. |
| 4 . | Use 95%Polidan®The mixture of TUX 100 and 5% CAT 10 catalyst is extruded into 18 × 2mm plastic tubes, cured in warm water at 95 °c for 12 hours, and the average value of all these plastic tube samples is taken. |
| 5 . | Typical values are obtained from plastic tube samples, which contain 95% Polidan®TUX 100 and 5% CAT 10 catalysts are extruded and cured in hot water at 95℃ for 12 hours. |
| 6 . | Use 95%Polidan®The mixture of TUX 100 and 5% CAT 10 catalyst is extruded into 18 × 2mm plastic tubes, cured in warm water at 95 °c for 12 hours, and the average value of all these plastic tube samples is taken. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7109M | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Manner Flexible PVC X3671A NAT 601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ULTEM™ 1000FC resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |
| UNISOFT TPE™ ST-55A-BK-3-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| NEOPLAST 145 FT EB | Zylog Plastalloys | TPV | NEOPLAST |