LNP™ FARADEX™ MS003 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AviTwT_LNPFARADEXMS003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Faradex* MS003 is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. Also known as: LNP* FARADEX* Compound MS-1003 Product reorder name: MS003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.2 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.3 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.3 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1200 | MPa | ASTM D638 |
| -- | 1300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 20.0 | MPa | ASTM D638 |
| Yield | 21.0 | MPa | ISO 527-2 |
| Fracture | 15.2 | MPa | ASTM D638 |
| Fracture | 15.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.2 | % | ASTM D638 |
| Yield | 5.2 | % | ISO 527-2 |
| Fracture | 88 | % | ASTM D638 |
| Fracture | 72 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1190 | MPa | ASTM D790 |
| -- | 1500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 27.6 | MPa | ASTM D790 |
| -- | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D256 |
| 23°C 2 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 80 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 22.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 92.2 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 53.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 56.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 9.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.7E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Static Decay 6 | 10 | msec | FTMS 101B |
| Shielding Effectiveness (3.00 mm) | 50 - 65 | dB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 232 - 249 | °C | |
| Mold Temperature | 32.2 - 54.4 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 25 - 50 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| 6 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2720SB | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Quantum Composites QC-2130 | Quantum Composites Inc. | Phenolic | Quantum Composites |
| Sinvicomp SRF3705Z | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| GLS PP YN06 MH1 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| LUVOCOM庐 1105-7786/L-BL | Lehmann & Voss & Co. | PEEK | LUVOCOM® |