LG ABS XR418
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ApIiOo_LGABSXR418.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Description
Application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ISO 1133 |
| shrinkage- Flow (3.20 mm) | 0.40 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 113 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 48.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2650 | MPa | ISO 178 |
| Flexural Stress 2 | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, unannealed, 4.00mm | 107 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed, 4.00mm | 90.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 108 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.0E-5 - 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.0E-5 - 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 230 - 240 | °C | |
| Nozzle Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 40 - 60 | °C | |
| Back Pressure | 0.981 - 2.94 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SSF4265UV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sindustris PC GN5002TF | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| UmaPET ULM (aesthetic) | Ester Industries Ltd. | PET | UmaPET |
| ELITE™ 5538G | The Dow Chemical Company | EPE | ELITE™ |
| LNP™ STAT-KON™ RX05489 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |