SABIC® SUPEER™ 8115
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® SUPEER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lSxGhx_SABICSUPEER8115.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® SUPEER™ 8115 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has good processablity. The grade offers better performance in terms of tensile properties, stiffness / toughness ratio and optical properties. Application Typical applications for SABIC® SUPEER™ 8115 are lamination film, frozen bags, liquid pouches, heavy duty bags, industrial liner, agriculture film, stretch hood, surface protective film. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.915 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 50 µm, blown film | 136 | MPa | ASTM D882 |
| 1% secant, TD : 50 µm, blown film | 151 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 52.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 650 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 730 | % | ASTM D882 |
| Dart Drop Impact 1(50 µm, Blown Film) | > 1000 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 15 | g | ASTM D1922 |
| TD : 50 µm, blown film | 24 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | 180 - 200 | °C | |
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured on blown film of 50 µm and BUR = 2.5 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene Lotrène® Q1018 H | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| Delta GPC-10 | Delta Polymers | PP Homopolymer | Delta |
| Hanwha Total PE P11CB | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| OTECH TPR OTR4595-Sandal | OTECH Corporation | TPE | OTECH TPR |
| Sylvin 9077-95C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |