RX® 611
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | RX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AkzW4R_RX-611.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RX® 611 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type MFH. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.20 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Compression Molded) | 80.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 16000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 130 | MPa | ISO 178 |
| Compressive Stress | 340 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (Compression Molded) | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 190 | °C | |
| 1.8 MPa, Annealed | > 282 | °C | |
| CLTE - Flow | 1.7E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.52 | W/m/K | ASTM C518 |
| RTI Elec | 180 | °C | UL 746 |
| RTI Imp | 180 | °C | UL 746 |
| RTI Str | 180 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 13 | kV/mm | ASTM D149 |
| Arc Resistance | 145 | sec | ASTM D495 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT7013-720UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Riteflex® UV655M | Celanese Corporation | TPC-ET | Riteflex® |
| Aplax P1017GN25 | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Hylac® FR134G10 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| POLYfill PP CIP6020F | Polykemi AB | PP, Unspecified | POLYfill |