Westlake LLDPE LF2010
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AIbq2W_Westlake-LLDPE-LF2010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake LF2010 is a hexene LLDPE with increased stiffness suitable for heavy duty films and shipping sacks. This material contains process aid for improved ease of extrusion, and can be blended with LDPE for strength property enhancements. Application/Uses Bags and sacks Agricultural films Trash bags and liners Co-extruded structures |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 255 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 290 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 44.8 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 41.4 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 900 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 210 | g | ASTM D1709A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.4 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.0 mils fabricated at 2.5:1 BUR. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 216 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE 56020 S XP | TOTAL Refining & Chemicals | HDPE, UHMW | TOTAL Polyethylene |
| Dynacom CT-140MT | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| Eco-Solutions GP325-1 | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| Karina BLACK PVC COMPOUND 850-48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Delene 3550 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |