ULTEM™ SILTEM-STM1500 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AGQM2H_ULTEM-SILTEM-STM1500-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SILTEM STM1500 is a flexible siloxane-polyetherimide copolymer for cable and wire coatings. RoHS compliant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (320°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 1.2 to 1.4 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 590 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 20.0 | MPa | |
| Break | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 15 | % | |
| Break | 110 | % | |
| Flexural Modulus 2 | 475 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| -- 4 | 18.0 | MPa | |
| -- 5 | 20.0 | MPa | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 60.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6 | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Unnotched Izod Impact Strength 7 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 75.0 | °C | ISO 306/B50 |
| -- | 78.0 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.1E-4 | cm/cm/°C | |
| Transverse : 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 4.7E+14 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 19 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 3.00 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 9.1E-3 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 175 | V | |
| Solution B | 100 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | V-1 | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 48 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 110 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 100 | °C | |
| Cylinder Zone 1 Temp. | 280 to 290 | °C | |
| Cylinder Zone 2 Temp. | 300 to 310 | °C | |
| Cylinder Zone 3 Temp. | 310 to 320 | °C | |
| Cylinder Zone 4 Temp. | 310 to 325 | °C | |
| Adapter Temperature | 315 to 325 | °C | |
| Melt Temperature | 285 to 320 | °C | |
| Die Temperature | 300 to 320 | °C | |
| Calibration Temp, First | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Break |
| 5 . | Yield |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VE VEEP 120 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | tefanyl® VE |
| ESTAPROP KUR 4000 CH/TD | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Estane® 2103-80AEF TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Kepital® TX-11H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| VALOX™ 325 resin | SABIC Innovative Plastics | PBT | VALOX™ |