TECHNYL® A 216 V30 BLACK 21N Datasheet,Nylon 66,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL® A 216 V30 Black 21N is a polyamide 66, reinforced with 30% of glass fiber, for injection moulding. This grade offers an excellent combination between thermal and mechanical properties.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Features	Good dimensional stability Good liquidity Good demoulding performance
Uses	Handle Large household appliances and small household appliances Connector Application in Automobile Field
Agency Ratings	EC 1907/2006 (REACH) UL QMFZ2
RoHS Compliance	RoHS compliance
Appearance	White Black Red Grey Natural color
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)
Resin ID (ISO 1043)	PA66-GF30

Physical	Dry	Conditioned	Unit	Test Method
Density	1.36	--	g/cm³	ISO 1183/A
Water Absorption				ISO 62
23°C, 24 hr	0.80	--	%	ISO 62
Saturated, 23°C	5.3	--	%	ISO 62
Equilibrium, 23°C, 50% RH	1.7	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	10000	7500	MPa	ISO 527-2/1A
Tensile Strength
Yield, 23°C	175	--	MPa	ASTM D638
Fracture, 23°C	190	135	MPa	ISO 527-2/1A
Tensile Elongation
Fracture, 23°C	3.3	--	%	ASTM D638
Fracture, 23°C	3.0	7.0	%	ISO 527-2
Flexural Modulus
23°C	9400	--	MPa	ASTM D790
23°C	9000	6350	MPa	ISO 178
Flexural Strength
23°C	260	--	MPa	ASTM D790
23°C	275	205	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	11	16	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength
23°C	75	90	kJ/m²	ISO 179/1eU
23°C	65	--	kJ/m²	ISO 179/1fU
Notched Izod Impact (23°C)	11	16	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	260	--	°C	ISO 75-2/Bf
1.8 MPa, not annealed	255	--	°C	ISO 75-2/Af
Melting Temperature	262	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	6.0E+15	1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+15	2.0E+15	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	40	30	kV/mm	IEC 60243-1
Relative Permittivity	3.75	4.00		IEC 60250
Dissipation Factor	0.010	0.11		IEC 60250
Comparative Tracking Index				IEC 60112
Solution a	600	600	V	IEC 60112
Solution B	500	500	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.6 mm)	HB	--		UL 94
Glow Wire Flammability Index				IEC 60695-2-12
1.6 mm	650	--	°C	IEC 60695-2-12
3.2 mm	750	--	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (1.6 mm)	650	--	°C	IEC 60695-2-13
Oxygen Index	23	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	270 - 280	°C
Middle Temperature	275 - 285	°C
Front Temperature	280 - 290	°C
Mold Temperature	70 - 100	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	AFnkXS_TECHNYLA216V30BLACK21N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SILIMIX 59D2	SILON s.ro	Siloxane, UHMW	SILIMIX
Sindustris PP HR2101D	Sincerity Australia Pty Ltd.	PP, Unspecified	Sindustris PP
Extreme™ D	Spartech Plastics	TPO	Extreme™
ELASTEL™ 1307-EI4-R1	HELLENIC CABLES S.A.	EPDM	ELASTEL™
Lustran® ABS 433	Styrolution	ABS	Lustran® ABS