RTP 209F
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AFABNA_RTP-209F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 209F is a nylon 12 reinforced with glass fiber. This material exhibits low water absorption, good dimensional stability, and improved low temperature resistance compared to most other nylons. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8960 | MPa | ASTM D638 |
| Tensile Strength | 148 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 8620 | MPa | ASTM D790 |
| Flexural Strength | 214 | MPa | ASTM D790 |
| Compressive Strength | 110 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 230 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 182 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 177 | °C | ASTM D648 |
| CLTE - Flow | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.50 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.016 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 4mil/in.Flammability, ASTM D-635: B in/min. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 221 - 254 | °C | |
| Middle Temperature | 221 - 254 | °C | |
| Front Temperature | 221 - 254 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® NXT PP-B A 2035/450 GF35 CP | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® NXT PP-B |
| Chemlon® 135 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Epic Urethane S7350 | Epic Resins | PUR, Unspecified | Epic Urethane |
| KOCETAL® TC701 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| ISOTHANE® 5085A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |