Polybilt™ Bitumen Modifier 106

Category:	LDPE , Low Density Polyethylene Resin
Manufacturer:	ExxonMobil Chemical
Trademark:	Polybilt™ Bitumen Modifier
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5a50at_Polybilt-Bitumen-Modifier-106.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Polybilt 106 is compatible with a large variety of bitumens. For optimum results a preliminary study is recommended to determine the base bitumen grade and optimum Polybilt 106 content to achieve the desired end-use properties. - Raises binder softening point and decreases penetration. - Substantially improves resistance to rutting. - Substantially improves resistance to jet fuels. - Improves binder low temperature flexibility and cohesion. Processing Conditions: Polybilt 106 pellets are free flowing, therefore, well suited for use in automated feeding and metering systems. Polybilt 106 can be blended easily using conventional equipment. Blending time will depend on the shear rate of the equipment used. Polybilt 106 can be pre-blended with bitumen or poured directly into the pugmill. Recommended blending temperature is 180 - 190°C (356 - 374°F).

Message

Polybilt 106 is compatible with a large variety of bitumens. For optimum results a preliminary study is recommended to determine the base bitumen grade and optimum Polybilt 106 content to achieve the desired end-use properties. - Raises binder softening point and decreases penetration. - Substantially improves resistance to rutting. - Substantially improves resistance to jet fuels. - Improves binder low temperature flexibility and cohesion. Processing Conditions: Polybilt 106 pellets are free flowing, therefore, well suited for use in automated feeding and metering systems. Polybilt 106 can be blended easily using conventional equipment. Blending time will depend on the shear rate of the equipment used. Polybilt 106 can be pre-blended with bitumen or poured directly into the pugmill. Recommended blending temperature is 180 - 190°C (356 - 374°F).

General Information
Additive	Heat Stabilizer
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Vinyl Acetate Content	24.0	wt%	ExxonMobil Method

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	50.0	°C	ASTM D1525

Resin Grade	Manufacturer	Category	Trademark
RTP EMI 262A	RTP Company	Nylon 6	RTP
Tenogel® ABS A3 HF NTLA010 AB308	Petropol Industry and Trade of Polymers LTDA	ABS	Tenogel® ABS
APEX® 94-A0098C-65	Teknor Apex Company	PVC, Flexible	APEX®
DJSilicone NE-651	DONGJUE SILICONE (NANJING) CO., LTD	Silicone	DJSilicone
3M™ Dyneon™ PTFE Compound 1191 N	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE Compound