GELOY™ CR7520 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AEopQQ_GELOYCR7520resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GELOY CR7520 is a general purpose injection moulding grade, blend of ASA/SAN. It can be positioned for outside parts in various markets, such as telecommunication, transportation, B&C, lighting and ID. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 7.00 | cm³/10min | ISO 1133 |
| 260°C/5.0 kg | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.40 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.55 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 30.0 | MPa | ISO 527-2/5 |
| Yield | 35.0 | MPa | ISO 527-2/50 |
| Fracture | 25.0 | MPa | ISO 527-2/5 |
| Fracture | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 2.5 | % | ISO 527-2/5 |
| Yield | 2.7 | % | ISO 527-2/50 |
| Fracture | 15 | % | ISO 527-2/5 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1900 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 155 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 85.0 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 75.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 85.0 | °C | ISO 306/B50 |
| -- | 90.0 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 5.20 | IEC 60250 | |
| 60 Hz | 5.20 | IEC 60250 | |
| 1 MHz | 3.21 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.15 | IEC 60250 | |
| 60 Hz | 0.15 | IEC 60250 | |
| 1 MHz | 0.026 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 600 | V | IEC 60112 |
| Solution B | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 19 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Nozzle Temperature | 220 - 250 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP521-187 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| MOSTEN FK 005 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Chiao Fu PA66 MD312G23 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Elastoprene 2561 | KMI Group, Inc. | SEBS | Elastoprene |
| Sylvin 9780-60UV Yellow 4213 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |