AMPLIFY™ TY 1151

Category:	MAH-g , Functional Polymer
Manufacturer:	The Dow Chemical Company
Trademark:	AMPLIFY™ TY
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ADSydR_AMPLIFY-TY-1151.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
AMPLIFY™ TY 1151 Functional Polymer is a maleic anhydride grafted (MAH) polymer intended for use in blends. In tie layers for flexible packaging, AMPLIFY TY 1151 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH) and other polar substrates. Typical blending levels in polyethylene let-down resin are 30-40% for adhesion to EVOH and 15-25% for adhesion to nylon. Main Characteristics: Excellent adhesion to polyamide and EVOH and polyethylene Excellent physical properties Wide range of process and service temperature For blown and cast film, and coating applications Complies with: U.S. FDA 21 CFR 175.105(c)(5) U.S. FDA 21 CFR 176.170(b)(2) U.S. FDA 21 CFR 176.180(b)(1) U.S. FDA 21 CFR 177.1520(with restrictions) Consult the regulations for complete details.

Message

AMPLIFY™ TY 1151 Functional Polymer is a maleic anhydride grafted (MAH) polymer intended for use in blends. In tie layers for flexible packaging, AMPLIFY TY 1151 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH) and other polar substrates.

Typical blending levels in polyethylene let-down resin are 30-40% for adhesion to EVOH and 15-25% for adhesion to nylon.

Main Characteristics:

Excellent adhesion to polyamide and EVOH and polyethylene

Excellent physical properties

Wide range of process and service temperature

For blown and cast film, and coating applications

Complies with:

U.S. FDA 21 CFR 175.105(c)(5)

U.S. FDA 21 CFR 176.170(b)(2)

U.S. FDA 21 CFR 176.180(b)(1)

U.S. FDA 21 CFR 177.1520(with restrictions)

Consult the regulations for complete details.

General Information
Agency Ratings	FDA 21 CFR 175.105 FDA 21 CFR 176.170 FDA 21 CFR 176.180 FDA 21 CFR 177.1520
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	0.920	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.5	g/10 min	ASTM D1238
MAH Graft Level ¹	Medium		Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ²			ASTM D638
Yield	12.0	MPa
Break	12.0	MPa
Tensile Elongation ³(Break)	800	%	ASTM D638
Flexural Modulus ⁴	276	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	97.0	°C	ASTM D1525
Melting Temperature (DSC)	124	°C	Internal Method

Note Message
1 .	Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt%
2 .	Molded in accordance with ASTM D4976.
3 .	Molded in accordance with ASTM D4976.
4 .	Molded in accordance with ASTM D4976.

Resin Grade	Manufacturer	Category	Trademark
POLYFORT® FPP 3551EU	A. Schulman Inc.	PP, Unspecified	POLYFORT®
ACCUTECH™ CP0437T40V	ACLO Compounders Inc.	PP Copolymer	ACCUTECH™
CGPC PVC R-11X MI Injection	China General Plastics Corporation	PVC, Flexible	CGPC PVC
KPOL-HDPE HD K-I 8/962	KPOL Chem Co.	HDPE	KPOL-HDPE
OTECH PVC OE9060 - Profile	OTECH Corporation	PVC, Unspecified	OTECH PVC