KMI PEI KM-H00R IEP
| Category: | PEI , Polyether Imide |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | KMI PEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EgvNty_KMIPEIKMH00RIEP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Performance Polyetherimide Material |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Across Flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 - 15 | % | ASTM D638 |
| Flexural Modulus | 3500 | MPa | ASTM D790 |
| Flexural Strength | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| Heat Distortion | 208 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 28 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-3931 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Formolene® LH6008 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| ESTADIENE 1030 T V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Karina YELLOW PVC COMPOUND 602D02/101-C-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| INFUSE™ 9900 | The Dow Chemical Company | OBC | INFUSE™ |