VITAMIDE® AS10NT6050
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ABp8UQ_VITAMIDE-AS10NT6050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AS10NT6050 is a Polyamide 66 (Nylon 66) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 2.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.6 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 35 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 125 | MPa | ISO 178 |
| Break | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 28 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 28.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | No Break | ASTM D256 | |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 27 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 575 | V | IEC 60112 |
| -- 3 | 575 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 26 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ LA543 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Abstron SE22 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| DJSilicone NE-7140 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| KOPA® KN1322G5V0 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Petrothene® Select GS707 | LyondellBasell Industries | LLDPE | Petrothene® Select |