Garaflex™ E 89-086-C3 NAT NF LCF-R
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | AlphaGary |
| Trademark: | Garaflex™ E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9b3r4s_Garaflex-E-89-086-C3-NAT-NF-LCF-R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GARAFLEX E 89-086-C3 NF LCF-R IS A 105°C RATED, LEAD FREE, FLEXIBLE CORD JACKET COMPOUND. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 to 1.24 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 78 to 84 | ||
| Shore A, 15 sec | 68 to 74 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 1.02 mm | 16.5 | MPa | |
| 1.91 mm | 15.2 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break, 1.91 mm | 340 | % | |
| Break, 1.02 mm | 320 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1(136°C, 168 hr) | 0.0 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 2(136°C, 168 hr) | -15 | % | UL Unspecified |
| Change in Tensile Strength 3(60°C, 168 hr, in ASTM #2 Oil) | 0.0 | % | UL Unspecified |
| Change in Ultimate Elongation 4(60°C, 168 hr, in ASTM #2 Oil) | -10 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -49.0 | °C | ASTM D746 |
| Deformation - retention, 1 hour (150°C, 1.27 mm) | 58 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 143 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 166 | °C | |
| Cylinder Zone 4 Temp. | 171 | °C | |
| Cylinder Zone 5 Temp. | 177 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 174 to 179 | °C | |
| Die Temperature | 177 | °C |
| Note Message | |
|---|---|
| 1 . | Thickness: 40 mil |
| 2 . | Thickness: 40 mil |
| 3 . | Thickness: 40 mil |
| 4 . | Thickness: 40 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E 398 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| ESTAPROP KUR 1060 GFC | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Dryflex® A2 600509 | ELASTO | SEBS | Dryflex® |
| ELASTOSIL® LR 3004/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| LNP™ THERMOCOMP™ QF0069 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |