LNP™ THERMOTUF™ PF00AIS compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9avbVh_LNP-THERMOTUF-PF00AIS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* PF00AIS is a compound based on Nylon 6 resin containing 50% Glass Fiber. Added features of this material include: Heat Stabilized, High Impact. Also known as: LNP* THERMOTUF* Compound PF-100-10 HI HS Product reorder name: PF00AIS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 151 | MPa | ASTM D638 |
| Flexural Modulus | 12300 | MPa | ASTM D790 |
| Flexural Strength | 248 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 204 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Modified Plastics MN 6/6-FG 20 | Modified Plastics, Inc. | Nylon 66 | Modified Plastics |
| Vipel® F017-AA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Witcom PP H/4L1-HS | Witcom Engineering Plastics B.V. | PP Homopolymer | Witcom PP |
| Bio-Flex® F 1110 | FKuR Kunststoff GmbH | Biodeg Polymers | Bio-Flex® |
| TECHNYL STAR® S 60G1 V30 GREY R7011 | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |