HANWHA LDPE 5326
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9aDcv5_HANWHA-LDPE-5326.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LDPE 5326 is manufactured by ICI autoclave high pressure process and designed for general purpose film. LDPE 5326 has well balanced property of mechanical and optical property. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 11.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 21.6 | MPa | ASTM D882 |
| TD : Break, 30 µm | 19.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 300 | % | ASTM D882 |
| TD : Break, 30 µm | 550 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 60 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 30.0 µm | 88.3 | kN/m | ASTM D1004 |
| TD : 30.0 µm | 78.5 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 87.0 | °C | ASTM D1525 |
| Melting Temperature | 111 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 - 170 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.025 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Q281 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| RheTech Thermoplastic Polyolefin FT2400-647UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Niche PA6BK | Niche Polymer, LLC | Nylon 6 | Niche |
| E-RIALFILL H 15 SJ 40 C1 | RIALTI Srl | PP Homopolymer | E-RIALFILL |
| Hostacom PPU X9067HS C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |