BJB Epoxy TC-1650 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9ZAGGR_BJB-Epoxy-TC-1650-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-1650 A/B is an aluminum powder filled epoxy casting resin system that provides service temperatures to 350°F (177°C). TC-1650 A/B is most commonly used for the construction of molds that require good heat conductivity, outstanding durability and provide production run capability. The majority of applications for TC-1650 A/B are used in conjunction with other materials in developing composite mold structures, however, the TC-1650 A/B is frequently used by itself. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Shrinkage | 0.20 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Demold Time (24 to 27°C) | 16.0 to 24.0 | hr | |
| Gel Time | 1.5 | hr | |
| Work Time 1(25°C) | 1.0 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 56.2 | MPa | ASTM D638 |
| Flexural Modulus | 7310 | MPa | ASTM D790 |
| Flexural Strength | 76.5 | MPa | ASTM D790 |
| Compressive Strength | 192 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 139 | °C | ASTM D648 |
| CLTE - Flow | 3.4E-5 | cm/cm/°C | ASTM D3386 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 7.0 | ||
| Shelf Life | 52 | wk | |
| Thermoset Mix Viscosity (25°C) | 15500 | cP | ASTM D2393 |
| Note Message | |
|---|---|
| 1 . | 1 lb mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4005A TFE 15 SI 2 | RTP Company | PPA | RTP |
| RC Plastics RCPCA25 | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | PC+ABS | RC Plastics |
| FERREX® GPP20CG42HB BLUE | Ferro Corporation | PP Homopolymer | FERREX® |
| TechnoElast V A6000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |
| Sylvin 2807-80 White 1437 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |