Plenco 06582 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Xt9gu_Plenco-06582-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 06582 is a rubber modified phenolic molding compound, offering excellent heat resistant properties, along with improved mechanical strength at elevated temperatures. UL recognized under component file E40654. 06582 is available in black. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.11 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 44 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9230 | MPa | ASTM D638 |
| Tensile Strength | 74.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 8910 | MPa | ASTM D790 |
| Flexural Strength | 115 | MPa | ASTM D790 |
| Compressive Strength | 157 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 45.5 | J/m | ASTM D256 |
| Notched Izod Impact | 47 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 241 | °C | ASTM D648 |
| Continuous Use Temperature | 230 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.2E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 13 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.077 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.00 mm) | V-0 | UL 94 | |
| Oxygen Index | 37 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.07%Drop Ball Impact, PLENCO Method: 276 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECAMID™ 66 | Ensinger Inc. | Nylon 66 | TECAMID™ |
| ANYPOL SE-2500P | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Karina GRAY PVC COMPOUND 880-18/402-F-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ DFL16E compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |
| Sylvin 7833-85 Brown 7457 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |