Durethan® BKV 50 H2.0 EF 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mtmpi8_DurethanBKV50H20EF900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.60 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.080 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.19 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.040 | -- | % | ISO 2577 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 232 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16200 | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 215 | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.7 | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 15000 | 9900 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 340 | 230 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.1 | 4.4 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-160, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | 85 | kJ/m² | ISO 179/1eU |
| 23°C | 100 | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 15 | -- | kJ/m² | ISO 180/1A |
| 23°C | 17 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 85 | 80 | kJ/m² | ISO 180/1U |
| 23°C | 85 | 80 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 3.40 | -- | J | ISO 6603-2 |
| 23°C | 4.30 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 1000 | -- | N | ISO 6603-2 |
| 23°C | 1180 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 180 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 214 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (23°C) | 7.0E+14 | 4.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 35 | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.70 | 12.9 | IEC 60250 | |
| 23°C, 1 MHz | 4.20 | 4.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.014 | 0.26 | IEC 60250 | |
| 23°C, 1 MHz | 0.017 | 0.077 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 | -- | V | IEC 60112 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO AES W210 | Techno Polymer Co, Ltd. | AES | TECHNO AES |
| SOLLAMID A 2750 FV | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| UBESTA 3024 GU6L1 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| NEXUS PC PC741 | Nexus Resin Group, LLC. | PC | NEXUS PC |
| Sylvin 9600-70 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |