EPIMIX POM GFR 25 NC
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPIMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9XoVQe_EPIMIX-POM-GFR-25-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYACETAL POM, reinforced with 25% of glass fiber , Standard-flow grad, for injection molding. POLYACETAL POM , is used in all sectors of industry, compliance with RoHs derivatives. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 4.00 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 0.70 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.40 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | -- | % | ISO 62 |
| Ash Content | 25 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 83 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7200 | 6900 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 100 | 90.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 3.0 | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 6950 | 6800 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 140 | 125 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 5.0 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 160 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 162 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 165 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 160 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 GI-1120 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Zytel® 101 NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Nypol® PA A3 G33 PRTA011 NR305 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Geon™ Vinyl Flexible XV3860 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| POCAN® KU 1-7625 901510 | LANXESS Asia/Pacific | PC+PBT | POCAN® |