Bayfit® 566 (80 Index, 2.8 pcf)
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayfit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Up9Cv_Bayfit-566-80-Index-2-8-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayfit 566 is a water-blown (MDI)/polyether based foam system used to manufacture high resilience (HR) cold-cure flex molded foam with medium to high load bearing properties. This system is characterized by good flow behavior in a wide variety of parts. Applications include office furniture, recreational seating, armrests and cushions. Bayfit 566 foam made at indices ranging from 80 to 105 typically passes the requirements of CAL-117 for flame resistance. Foams made at higher indices typically do not. As with any product, use of the Bayfit 566 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.0449 | g/cm³ | ASTM D3574 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 0.0758 | MPa | ASTM D3574 |
| Tensile Elongation (Break) | 120 | % | ASTM D3574 |
| Tear Resistance | 357.2 | g/2.5 cm | ASTM D3574 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compression Set | ASTM D3574 | ||
| 50% | 3.6 | % | ASTM D3574 |
| 70% | % | ASTM D3574 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| IFD | ASTM D3574 | ||
| 25% R : 102 mm | 21.0 | lb/50 in² | ASTM D3574 |
| 65% R : 102 mm | 59.0 | lb/50 in² | ASTM D3574 |
| SAG Factor - 65%/25% IFD | 2.80 | ASTM D3574 | |
| Part A Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity: 28 cps Part B Appearance: Slightly hazy liquid Specific Gravity @ 25°C: 1.02 Viscosity: 1100 cps Cream Time: 10 secGel Time: 50 secFree Rise Density: 2.5 lb/ft³Component Temperature: 75 to 90°FMold Temperature: 100 to 130°FDemold Time: 3.5 to 5 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® NX4001A | Custom Resins Group | Nylon 6 | Nylene® |
| AKROMID® B3 GK 30 black (3788) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| DJSilicone NE-G121 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| HAIPLEN H50 C6 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Hifax TRC 432P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |