SLOVALEN® PH 66 GF 30 FRO 4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9OF1Ey_SLOVALEN-PH-66-GF-30-FRO-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified PP homopolymer for injection molding, chemically reinforced with 30% glass fiber, contains modifier mechanical properties. Reduced flammability. Increased stiffness of PP compared to non-compliance. Application in all industries. Modification increased rigidity, toughness, modulus of elasticity. Supplied in natural finish and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.1 | % | |
| Flow | 0.68 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 5600 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 37 | kJ/m² | |
| 23°C | 39 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 163 | °C | ISO 306/B |
| Melting Temperature (DSC) | 160 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-1 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics EL-636 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Xuchuan XCW-8065DY | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Karina BLACK PVC COMPOUND -E CAK 85-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ IFL21 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |
| ADLAS® O07FJEGX00 | A.D. Compound S.p.A. | PP Copolymer | ADLAS® |