Ebalta GM 973 / Comp. A+B

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Ebalta Kunststoff GmbH
Trademark:	Ebalta
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TsT9QG_Ebalta-GM-973-Comp-A-B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
The product is a Polyurethane system. For improving of the flow characteristics, GM 973 can be preheated to approx. 30°C. The final strength is achieved at room temperature after approx. 3-5 days. By post-curing at 80°C for 5 hours the stated values are achieved in short time. Parts / moulds must not be cast with addition curing silicone, since this might lead to faulty reactions when curing the silicone. Applications Flexible parts fixtures Properties shore A hardness 90 high tear strength well castable flexible dyeable

Message

The product is a Polyurethane system.
For improving of the flow characteristics, GM 973 can be preheated to approx. 30°C.
The final strength is achieved at room temperature after approx. 3-5 days.
By post-curing at 80°C for 5 hours the stated values are achieved in short time.
Parts / moulds must not be cast with addition curing silicone, since this might lead to faulty reactions when curing the silicone.

Applications

Flexible parts

fixtures

Properties

shore A hardness 90

high tear strength

well castable

flexible

dyeable

General Information
Features	Good Colorability Good Flexibility High Strength
Appearance	Beige
Processing Method	Casting

Hardness	Nominal Value		Test Method
Shore Hardness (Shore A)	87 to 93		ISO 7619

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	14.0 to 18.0	MPa	ISO 527-2
Tensile Strain (Break)	500 to 600	%	ISO 527-2

Elastomers	Nominal Value	Unit	Test Method
Tear Strength	50 to 60	kN/m	ISO 34-1

Thermoset	Nominal Value	Unit
Thermoset Components
Hardener	Mix Ratio by Weight: 15
Resin	Mix Ratio by Weight: 100

Uncured Properties	Nominal Value	Unit
Density (20°C)	1.06 to 1.10	g/cm³
Viscosity (25°C)	4.0 to 5.0	Pa·s
Curing Time (20°C)	12 to 16	hr
Pot Life ¹(20°C)	12 to 15	min

Note Message
1 .	200 g

Resin Grade	Manufacturer	Category	Trademark
Mapex AT0620GB	Ginar Technology Co., LTD.	Nylon 66	Mapex
RTP 206D	RTP Company	Nylon 612	RTP
Tufpet PBT G1010	Mitsubishi Rayon America Inc.	PBT	Tufpet
APEX® 3210-90NT	Teknor Apex Company	PVC, Flexible	APEX®
LONGLITE® LCP LCP-300 N5TL	CCP Group	LCP	LONGLITE® LCP