EQUATE PE EFDC-7087
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | EQUATE Petrochemical Company KSCC |
| Trademark: | EQUATE PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Knrso_EQUATE-PE-EFDC-7087.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EFDC-7087 is a linear low-density polyethylene (LLDPE) resin for tubular blown film extrusion. Films made from EFDA-7087 have good toughness, high tensile strength and outstanding puncture resistance. EFDA-7087 contains high levels of slip and antiblocking agent. The product offers excellent draw down capability for thinner gauge film production. The films have good sealability and machinability for easy conversion on high-speed machines. EFDC-7087 is recommended for the manufacture of thin gauge liner films, garment bags and other industrial and consumer packaging applications requiring toughness and puncture resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Bulk Density | 530 | kg/m³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 193 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 221 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 34.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 26.0 | MPa | ASTM D882 |
| Dart Drop Impact (Blown Film) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.0 µm | 35.0 | kN/m | ASTM D1922 |
| TD : 25.0 µm | 135.0 | kN/m | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Energy (25.0 µm) 2 | 700 | J/cm | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 14 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 | °C | |
| Cylinder Zone 2 Temp. | 185 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 185 | °C | |
| Adapter Temperature | 185 | °C | |
| Melt Temperature | 185 | °C | |
| Die Temperature | 185 | °C |
| Extrusion instructions |
|---|
| Die Gap: >1.8 mm |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niblan VCF30 | Soredi S.p.a. | PBT | Niblan |
| Osterlene® MI-13-1.4 | Osterman & Company | PS (MIPS) | Osterlene® |
| POLYCASA® ACRYL G 77 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |
| ESTOPLAST XU 6250GY01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| SIBUR Synthetic Rubber SBR-1723 Grade B | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |