Larpeek 10 G/15
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larpeek |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Kl7kV_Larpeek-10-G-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyetheretherketone (PEEK). UL94 V-0 classified, halogens free. Glass fibres. Very good chemical resistance. Very good thermal resistance. Low smoke toxicity index and optical density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 1.0 | % | |
| Flow : 2.00 mm | 0.40 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 6300 | MPa | |
| 60°C | 6100 | MPa | |
| 90°C | 5700 | MPa | |
| 120°C | 5500 | MPa | |
| 150°C | 5100 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 90°C | 110 | MPa | |
| Yield, 120°C | 95.0 | MPa | |
| Yield, 150°C | 70.0 | MPa | |
| Break, 23°C | 135 | MPa | |
| Break, 60°C | 125 | MPa | |
| Break, 90°C | 110 | MPa | |
| Break, 120°C | 90.0 | MPa | |
| Break, 150°C | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 90°C | 3.0 | % | |
| Yield, 120°C | 3.0 | % | |
| Yield, 150°C | 3.5 | % | |
| Break, 23°C | 2.8 | % | |
| Break, 60°C | 3.1 | % | |
| Break, 90°C | 3.4 | % | |
| Break, 120°C | 3.8 | % | |
| Break, 150°C | 4.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 290 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 285 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 220 | °C | |
| Vicat Softening Temperature | > 300 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 370 to 400 | °C | |
| Mold Temperature | 170 to 200 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-300 | Teknor Apex Company | TPE | Medalist® |
| TECHNYL® A 216 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Tenopom® POM B3 MF TZ NTLA010 PR318 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| KOPA® KN133G30HSBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LEXAN™ 101 resin | SABIC Innovative Plastics | PC | LEXAN™ |