DOWLEX™ 2107GC
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9FMm40_DOWLEX-2107GC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2107GC is processable at high line speeds. Films made from DOWLEX 2107GC Polyethylene Resin exhibit excellent stretchability, outstanding tear and impact resistance, as well as exceptional optical properties. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 23 µm | 6.30 | MPa | ASTM D882 |
| TD : Yield, 23 µm | 5.90 | MPa | ASTM D882 |
| MD : Break, 23 µm | 43.0 | MPa | ASTM D882 |
| TD : Break, 23 µm | 28.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 23 µm | 470 | % | ASTM D882 |
| TD : Break, 23 µm | 900 | % | ASTM D882 |
| Dart Drop Impact 3(23 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 23 µm | 410 | g | ASTM D1922 |
| TD : 23 µm | 540 | g | ASTM D1922 |
| Film tensile properties-maximum stretch to penetration 5 | 130 | % | Internal method |
| Film Tensile Properties-Maximum Elongation 6 | 240 | % | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm) | 92 | ASTM D2457 | |
| Haze (23.0 µm) | 0.70 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: Melt Temperature: 220-280°C Chill Roll Temperature: 20-60°C Line Speed 150-450 m/min Recommended Gauge Range: 10-60 µm |
| Note Message | |
|---|---|
| 1 . | Cast film, 250 m/min; Chill roll 25°C. |
| 2 . | Cast film, 250 m/min; Chill roll 25°C. |
| 3 . | Cast film, 250 m/min; Chill roll 25°C. |
| 4 . | Method B; Cast film, 250 m/min; Chill roll 25°C. |
| 5 . | Cast film, 250 m/min; Chill roll 25°C; Measured on test stand; Max pre-strech before sharp probe penetrates. |
| 6 . | Cast film, 250 m/min; Chill roll 25°C; Measured on test stand. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPC-40G Black | PolyOne Corporation | PP Copolymer | Maxxam™ |
| POLYPRO® CB5108H | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| Stretchene RP1903 | LyondellBasell Industries | PP Random Copolymer | Stretchene |
| Sylvin 8240-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MOSTEN MA 350 | UNIPETROL RPA | PP Homopolymer | MOSTEN |