Borlink™ LE0315
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wfgOKf_Borlink-LE0315.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Borlink LE0315 is a crosslinkable black polyethylene compound, specially designed for semiconductive strippable insulation screen of energy cables. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ASTM D1505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 11.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 250 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | 1.1 | kN/m |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (121°C, 168 hr) | > 25 | % | ASTM D638 |
| Change in Ultimate Elongation in Air (121°C, 168 hr) | > 100 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -35.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D991 | ||
| 23°C | 50 | ohms·cm | |
| 90°C | 1.0E+2 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB50 NL IT | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Chemlon® 100 W | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| INEOS PP 200-NA02 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| ISPLEN® PM 460 AS | REPSOL | PP Homopolymer | ISPLEN® |
| Karina IVORY PVC COMPOUND TR-601D35/1-Y-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |