Braskem PE GM 5010 T2 B
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 92HHvW_Braskem-PE-GM-5010-T2-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GM5010T2B is a High Density Polyethylene compounding specially developed for the manufacturing of extruded pipes for water distribution. It is produced with bimodal technology and has high molar mass. It shows high mechanical properties and has excellent resistance to hydrostatic pressure and to stress cracking. This resin has MRS (Minimum Required Strength) of 8 MPa, according to ISO 9080, and is classified as PE 80, according to ISO 12162. GM5010T2B is manufactured in blue color and contains additives to protect it against ultraviolet radiation action and photodegradation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.947 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.45 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 22.0 | MPa | |
| Break, Compression Molded | 36.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, Compression Molded | 12 | % | |
| Break, Compression Molded | 910 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 1090 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 260 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 69.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 2304 | Huntsman Corporation | PAO | REXtac® APAO |
| TEKNIFLEX® Pouch PE2718 | Tekni-Films, a div of Tekni-Plex | Film, Polyester/PE/Al Foil/LLDPE | TEKNIFLEX® Pouch |
| Haysite Plastics Heatmeiser® | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| HiFill® PA6 IM L N | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ THERMOCOMP™ Lexan_LGK3020 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |