LNP™ STAT-LOY™ N30009 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 91axS2_LNP-STAT-LOY-N30009-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY N30009 is a compound based on PC+ABS Blend resin. Added features of this material include: Antistat, Flame Retardant. Also known as: LNP* STAT-LOY* Compound PCA-FR Product reorder name: N30009 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.53 to 0.65 | % | |
| Across Flow : 24 hr | 0.53 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2150 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 55.0 | MPa | |
| Break | 49.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 100 | % | |
| Flexural Modulus | 2150 | MPa | ASTM D790 |
| Flexural Strength | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 38.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 100 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 199 to 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-G33 | Polymer Resources Ltd. | Nylon 66 | PRL |
| Scolefin 52 T 10-9 | Ravago Group | PP Homopolymer | Scolefin |
| Ad-Tech Polyester NO. 26 | Ad-Tech Plastic Systems Corp. | Polyester, TS | Ad-Tech Polyester |
| ELASTOSIL® E 41 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| Karina IVORY PVC COMPOUND 105909-35/ 1-DY-ACE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |