TECHNYL® A 246M BLACK 21 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h9hGus_TECHNYL-A-246M-BLACK-21-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 246M Black 21 N is an unfilled polyamide 6.6, impact modified, for injection molding. The product is available in black color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.9 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1900 | 600 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield | 50.0 | -- | MPa | ASTM D638 |
| Yield | 47.0 | 42.0 | MPa | ISO 527-2/1A |
| Break | 44.0 | 35.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ||||
| Yield | 20 | 210 | % | ISO 527-2/1A |
| Break | 80 | -- | % | ASTM D638 |
| Flexural Modulus | 1800 | -- | MPa | ASTM D790 |
| Flexural Strength | ||||
| -- | 70.0 | -- | MPa | ASTM D790 |
| -- | 70.0 | 27.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 97 | 100 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ||||
| -30°C | 16 | -- | kJ/m² | ISO 179/1fU |
| 23°C | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ||||
| 23°C | 1.0 | 120 | J/m | ASTM D256 |
| -30°C | 22 | -- | kJ/m² | ISO 180/1A |
| 23°C | 60 | 80 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 63.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 38 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.20 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.060 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 575 | 600 | V | |
| Solution B | 450 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Oxygen Index | 25 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Small Boss SPVC8013 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Unspecified | Small Boss |
| Unichem 8634 | Colorite Polymers | PVC, Unspecified | Unichem |
| Alpha PVC 7762 NATURAL | AlphaGary | PVC, Unspecified | Alpha PVC |
| KYOCERA CT4150 | KYOCERA Chemical Corporation | PI, TS | KYOCERA |
| SABIC® PP 532Bh | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |