LNP™ STAT-LOY™ 9X05426C compound
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8q4901_LNP-STAT-LOY-9X05426C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat. Also known as: LNP* STAT-LOY* Compound PDX-05426 CCS BL5-343-2 TP Product reorder name: 9X05426C |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.98 | % | ISO 294-4 |
| Flow : 24 hr | 0.82 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1750 | MPa | ASTM D638 |
| -- | 1480 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 42.7 | MPa | ASTM D638 |
| Yield | 42.0 | MPa | ISO 527-2 |
| Break | 40.7 | MPa | ASTM D638 |
| Break | 39.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.7 | % | ASTM D638 |
| Yield | 6.2 | % | ISO 527-2 |
| Break | 18 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1660 | MPa | ASTM D790 |
| -- | 1410 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 55.2 | MPa | ASTM D790 |
| -- | 44.8 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 540 | J/m | ASTM D4812 |
| 23°C 3 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 2.85 | J | ASTM D3763 |
| -- | 0.772 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 79.4 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 79.5 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 67.8 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 70.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 to 1.0E+11 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.0 to 88.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 215 to 238 | °C | |
| Middle Temperature | 215 to 238 | °C | |
| Front Temperature | 215 to 238 | °C | |
| Nozzle Temperature | 215 to 238 | °C | |
| Mold Temperature | 23.0 to 88.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP5904 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Epoxies, Ect. 10-3046 NS | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Kumho KBR 710S | Korea Kumho Petrochemical Co., Ltd. | PBR, Low Cis | Kumho KBR |
| Polygen SC75D | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| TARFLON™ #1700 | Formosa Idemitsu Petrochemical Corporation | PC | TARFLON™ |