Nypol® PA A3 G20 HS NTLA013 NR437
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8KX2Gz_Nypol-PA-A3-G20-HS-NTLA013-NR437.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 20% of fiberglass and term stabilized, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.26 to 1.29 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.85 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.0 to 1.2 | -- | % | ASTM D570 |
| Ash Content | 18 to 22 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7420 | 5400 | MPa | ASTM D638 |
| Tensile Strength | 140 | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.4 | 7.0 | % | ASTM D638 |
| Flexural Modulus | 6500 | 4180 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 60 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 248 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zetpol® 2000 | Zeon Corporation | NBR | Zetpol® |
| Capilene® S 89 E | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Halene H M5002L | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| LG EVA EC15006 | LG Chem Ltd. | EVA | LG EVA |
| SABIC® FORTIFY™ C5070D | Saudi Basic Industries Corporation (SABIC) | TPO (POE) | SABIC® FORTIFY™ |