LNP™ THERMOCOMP™ EC006APQ compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8BdsdZ_LNP-THERMOCOMP-EC006APQ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP EC006APQ is a compound based on Polyetherimide containing 30% Carbon Fiber. Added features include: Electrically Conductive, High Flow. Also known as: LNP* THERMOCOMP* Compound EC006APQ Product reorder name: EC006APQ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/6.7 kg) | 69 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.030 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.11 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 30500 | MPa | ASTM D638 |
| -- | 29300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 281 | MPa | ASTM D638 |
| Fracture | 252 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 1.1 - 1.3 | % | ASTM D638 |
| Fracture | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 26300 | MPa | ASTM D790 |
| -- 5 | 23900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 332 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 350 | MPa | ASTM D790 |
| Compressive Strength | 231 | MPa | Internal method |
| Shear Modulus | 4730 | MPa | ASTM C273 |
| Shear Strength | 128 | MPa | ASTM C273 |
| Poisson's Ratio | 0.44 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 82 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 710 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 195 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 150°C | 7.0E-6 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 150°C | 5.0E-6 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 380 - 400 | °C | |
| Middle Temperature | 380 - 400 | °C | |
| Front Temperature | 380 - 400 | °C | |
| Processing (Melt) Temp | 380 - 400 | °C | |
| Mold Temperature | 165 - 180 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Injection Speed: 40 - 70 mm/s |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 20 EG | RTP Company | Nylon 66 | RTP |
| RTP 800 GB 25 DEL | RTP Company | Acetal (POM) Copolymer | RTP |
| Tenite™ Propionate 307E4000018 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| LUVOCOM® 1105-7301 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Ingeo™ 3D850 | NatureWorks® LLC | PLA | Ingeo™ |