Westlake LDPE EF602
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 82lsfv_Westlake-LDPE-EF602.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake EF602 is a fractional melt LDPE with excellent toughness. It is suggested in heavy duty films and shipping sacks, and in industrial shrink applications. It can be used as a bubble stabilizer in LLDPE rich films. Application/Uses: Heavy duty refuse bags & liners Industrial shrink film Bundling and casewrap |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 165 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 217 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 17.2 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 10.3 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 150 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 680 | % | ASTM D882 |
| Dart Drop Impact 4(51 µm, Blown Film) | 130 | g | ASTM D1709 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 2.0 mils; blow up ratio 2.5:1, die gap 35 mils.Melt temperatures of 360° F - 400° F are recommended for Westlake Chemical EF602 with blow-up ratios of 1.5:1 or higher. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flex® TPE A5001 LC | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| LNP™ COLORCOMP™ DX06407H compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| MAJORIS GFR307 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| REPOL® SS80N | Reliance Industries Limited | PP Homopolymer | REPOL® |
| UNITIKA Nylon 6 M1030B | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |