TOTAL Polystyrene 260-75
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7zgCs4_TOTAL-Polystyrene-260-75.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Compound 260-75 is an easy flow, HB recycled high impact polystyrene for injection molding application. It contains 75% of recycled polystyrene. It is recommended for the manufacturing of articles which require good dimensional stability. Applications:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 - 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 - 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| Balance | < 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 22.0 - 30.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 30 - 55 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 1700 - 2300 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, injection molding | 69 - 88 | J/m | ASTM D256 |
| 23°C, injection molding | 7.6 - 9.8 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 - 95.0 | °C | ISO 306/A50, ASTM D1525 1 |
| Heat Distortion | |||
| -- | 70 - 85 | °C | ISO 75-2 |
| -- | 70 - 85 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 210 - 230 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 200 to 220°C |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6FLZ (Series: FR/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| NaturePlast NP DU 103 | NaturePlast | Nylon 1012 | NaturePlast |
| Adell Polyamide AO-36 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| DJSilicone NE-161 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| ELEVATE™ EF439 | Westlake Chemical Corporation | EVA | ELEVATE™ |