Dow Corning® C6-235

Category:	Silicone , Silicone
Manufacturer:	Dow Corning Corporation
Trademark:	Dow Corning®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7qnAih_DowCorningC6235.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
High consistency rubber raw materials for healthcare industry fabrication APPLICATIONS Dow Corning® Class VI Elastomers (C6-235, C6-250, C6-265) are uncatalyzed silicone elastomer bases designed for compounding into elastomer for part fabrication and medical devices, including those intended for implantation in humans for up to 29 days. DESCRIPTION Dow Corning Class VI Elastomers (C6-235, C6-250, C6-265) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a catalyst is necessary to accomplish cure. The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, shore A durometer). These materials may be blended if desired to achieve intermediate hardnesses. After appropriate compounding with a catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

Message

High consistency rubber raw materials for healthcare industry fabrication

APPLICATIONS
Dow Corning® Class VI Elastomers (C6-235, C6-250, C6-265) are uncatalyzed silicone elastomer bases designed for compounding into elastomer for part fabrication and medical devices, including those intended for implantation in humans for up to 29 days.

DESCRIPTION
Dow Corning Class VI Elastomers (C6-235, C6-250, C6-265) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a catalyst is necessary to accomplish cure. The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, shore A durometer). These materials may be blended if desired to achieve intermediate hardnesses.
After appropriate compounding with a catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

General Information
Features	High Gas Permeability Good coloring High pressure heating resistance
Uses	Composite Medical/nursing supplies
Agency Ratings	ISO 10993-Part I USP Class VI
Processing Method	Composite

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.12	g/cm³	ASTM D792
Molding Shrinkage - Flow	2.1	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	37		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (200% Strain)	1.50	MPa	ASTM D412
Tensile Strength	8.50	MPa	ASTM D412
Tensile Elongation (Break)	1100	%	ASTM D412
Tear Strength ¹	37.0	kN/m	ASTM D624

Note Message
1 .	B mould

Resin Grade	Manufacturer	Category	Trademark
Retpol® 3013 HS UV3	PolyPacific Pty. Ltd.	PP, Unspecified	Retpol®
Supol HT125E	LyondellBasell Industries	PP Copolymer	Supol
Nycal™ 1850RMC40	Technical Polymers, LLC	Nylon 6	Nycal™
ELASTOSIL® M 4541	Wacker Chemie AG	Silicone	ELASTOSIL® M
PENTALLOY BP H black	PENTAC Polymer GmbH	Nylon 6+PP	PENTALLOY BP