POCAN® B 3235 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PwBZzg_POCAN-B-3235-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 30 % glass fibers, injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.55 1.55 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 2.00 mm 1 | 1.1 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.20 | % | |
| Flow : 260°C, 2.00 mm 3 | 0.40 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 0.10 | % | |
| Viscosity Number (Reduced Viscosity) | 95.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 190 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 9500 | MPa | ASTM D638 |
| 23°C | 9800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break, 23°C | 133 | MPa | ASTM D638 |
| Break, 23°C | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break, 23°C | 2.5 | % | ASTM D638 |
| Break, 23°C | 2.9 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 9800 | MPa | |
| 1000 hr | 8900 | MPa | |
| Flexural Modulus | |||
| 23°C | 7600 | MPa | ASTM D790 |
| 23°C 5 | 9800 | MPa | ISO 178/A |
| Flexural Strength | |||
| 23°C | 190 | MPa | ASTM D790 |
| 23°C 6 | 225 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.4 | % | ISO 178/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behavior 8 | passed | ISO 3795 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GHMR, 09-100, GF30 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | |
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 2.50 | J | |
| 23°C | 2.30 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 165 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 9 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.1E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.26 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (23°C, 1.00 mm) | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 4.00 | ||
| 23°C, 1 MHz | 3.80 | ||
| Comparative Tracking Index (Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index 10 | 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| 10 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M20TCPP20 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| UBESTA 3030 JI9L | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Niche PA6GF33N | Niche Polymer, LLC | Nylon 6 | Niche |
| LNP™ LUBRICOMP™ ZI001 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |
| LUVOCOM® 50-9310 | LEHVOSS Group | PC | LUVOCOM® |