Ingeo™ 3D860
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7nLe3B_Ingeo3D860.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ingeo™ 3D860 is a grade developed for manufacturing 3D printer monofilament. Engineered to deliver improved heat-resistance and high impact strength to 3D printed parts, this formulated grade achieves thermal and mechanical properties similar to ABS while offering an alternative to styrenic-based materials. Monofilaments made with Ingeo 3D860 provide excellent 3D printing characteristics such as precise detail, good adhesion to build plates, less warping or curling, and low odor. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 5.0 - 7.0 | g/10 min | ASTM D1238 |
| Relative Viscosity 1(30°C) | 4.00 | ASTM D5225 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2400 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 32.8 | MPa | ASTM D638 |
| -- | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 2.3 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5 | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 6(0.45 MPa, Unannealed) | 80.0 - 90.0 | °C | ASTM E2092 |
| Glass Transition Temperature | 55.0 - 60.0 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 165 - 180 | °C | ASTM D3418 |
| Additional Information |
|---|
| 3D Printing Temperature: 190 to 230°CAnnealing Temperature: 80 to 130°CPrint Bed Temperature: None needed (or 50 to 70°C if applicable) |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 179 | °C | |
| Cylinder Zone 2 Temp. | 191 | °C | |
| Cylinder Zone 3 Temp. | 199 | °C | |
| Adapter Temperature | 199 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 199 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 20 to 150 rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 g/dL in chloroform |
| 2 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 3 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 4 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 5 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 6 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SGF 40 NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| TRIBOCOMP® POM CF10 TS0 | EPIC Polymers | Acetal (POM) Copolymer | TRIBOCOMP® |
| ACCUTECH™ CP0436M40CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| HIVAL® HG6 Natural | Nexeo Solutions, LLC. | ABS | HIVAL® |
| Huafon JF-W-AH6065 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |