PRL PC-BR1-UV
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7i4rdR_PRL-PC-BR1-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC-BR1-UV is a polycarbonate (PC) product,. It can be processed by blow molding or extrusion and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 1.0 - 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 70 | ASTM D785 | |
| Class r | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18mm | 62.1 | MPa | ASTM D638 |
| Fracture, 3.18mm | 66.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18mm | 7.0 | % | ASTM D638 |
| Fracture, 3.18mm | 120 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2310 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 750 | J/m | ASTM D256 |
| Dart Drop Impact (3.18 mm) | > 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 129 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 1 |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI (1.50 mm) | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 - 124 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 299 - 321 | °C | |
| Cylinder Zone 2 Temp. | 310 - 332 | °C | |
| Cylinder Zone 3 Temp. | 321 - 343 | °C | |
| Melt Temperature | 316 - 343 | °C | |
| Die Temperature | 82.2 - 116 | °C |
| Extrusion instructions |
|---|
| Do not exceed 8 hour drying time.Mold Temperature: 180° to 240°F |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICTREX® ST™ P45 | Victrex plc | PEKEKK | VICTREX® ST™ |
| Celstran庐 PA66-GF50-20 AD3007 | Celanese Corporation | Nylon 66 | Celstran® |
| Exact™ 9071 | ExxonMobil Chemical | Plastomer | Exact™ |
| POLYFORT® FIPP MKF 4025 | A. Schulman Europe | PP Copolymer | POLYFORT® |
| LNP™ THERMOCOMP™ RF006LXP compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |