ULTEM™ DH1004 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7gE7bF_ULTEMDH1004resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. RoHS compliant and UL94 V0 listed. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2900 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 95.0 | MPa | ASTM D638 |
| Yield | 97.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 90.0 | MPa | ASTM D638 |
| Fracture | 80.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Fracture 5 | 85 | % | ASTM D638 |
| Fracture | 80 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3000 | MPa | ASTM D790 |
| -- 7 | 2800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 136 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| -30°C 9 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 11 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Reverse Notch Izod Impact (3.20 mm) | 3300 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -20°C, Total Energy | 88.0 | J | ASTM D3763 |
| 0°C, Total Energy | 99.0 | J | ASTM D3763 |
| 23°C, Total Energy | 88.0 | J | ASTM D3763 |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | 90 | % | ASTM D3763 |
| 0°C | 100 | % | ASTM D3763 |
| 23°C | 100 | % | ASTM D3763 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| NBS Smoke Density - Flaming, Ds, 4 min | 0.700 | ASTM E662 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 214 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 12 | 205 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 6.40mm | 204 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 190 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ISO 306/A50 |
| -- | 212 | °C | ISO 306/B50, ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -20 to 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -20 to 150°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 | |
| Oxygen Index | 46 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 - 8.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 330 - 390 | °C | |
| Middle Temperature | 335 - 390 | °C | |
| Front Temperature | 345 - 390 | °C | |
| Nozzle Temperature | 345 - 390 | °C | |
| Processing (Melt) Temp | 355 - 390 | °C | |
| Mold Temperature | 130 - 160 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® FL 34 E | Versalis S.p.A. | LDPE | Riblene® |
| RTP 203 | RTP Company | Nylon 66 | RTP |
| SEPAZ™ LH60 | Mando Advanced Materials Co., Ltd. | PP Homopolymer | SEPAZ™ |
| Ultramid® A3HG7 | BASF Corporation | Nylon 66 | Ultramid® |
| MAXAMID™ EPDM206-NC010 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |